M. Davood Yavari; H. Haeri; V. Sarfarazi; M. Fatehi Marji; H. A. Lazemi
Abstract
The propagation mechanism of cracks emanating from two holes within the concrete specimens is studied by considering the effects of different lateral compressive stresses. The experimental part of this research work is carried out on some specially prepared pre-cracked specimens with two neighbouring ...
Read More
The propagation mechanism of cracks emanating from two holes within the concrete specimens is studied by considering the effects of different lateral compressive stresses. The experimental part of this research work is carried out on some specially prepared pre-cracked specimens with two neighbouring holes under only a uniaxial compression in the laboratory. The numerical modeling part is performed under both the uniaxial compresion and the lateral confinment by the 2D particle flow code (PFC2D). It is shown that the lateral confinement may change the path of crack propagation in a specimen compared to that of the uniaxially-loaded one. Various senarios of the mixed mode radial crack propagation around the holes are obtained, and both the wing (induced tensile) cracks and secondary (shear) cracks are produced and propagated in various paths due to a change in the confining pressure. The fracturing pattern changes from a single tensile crack to that of the several shear bands by increasing the confining pressure. Also the number of shear cracks is increased by increasing the lateral confinement.On the other hand, as the confining pressure increases, the wing cracks start their growth from the walls and reach the center of the cracks under high confinements.
M. Davood Yavari; H. Haeri; V. Sarfarazi; M. Fatehi Marji; H. A. Lazemi
Abstract
Investigating the crack propagation mechanism is of paramount importance in analyzing the failure process of most materials. This process may be exposed during each kind of loading on the materials. In this work, the cracking mechanism in rock-like materials is studied using the numerical methods and ...
Read More
Investigating the crack propagation mechanism is of paramount importance in analyzing the failure process of most materials. This process may be exposed during each kind of loading on the materials. In this work, the cracking mechanism in rock-like materials is studied using the numerical methods and compared with the experimental test results. However, the mechanism of crack growth in brittle materials such as rocks is influenced by different parameters. This research work focuses on the effect of the initial crack angles on the crack growth paths of these materials. Some cubic samples containing pre-existing cracks are tested in compression by considering different flaw orientations. The specimens are made of cement, water, and sand. Moreover, the mentioned process is numerically simulated using three different methods: the finite difference method for discontinuous bodies or discrete element method, the displacement discontinuity method, and the versatile finite element method. The micro-parameters for simulation are gained by the trial-and-error procedure for the discrete element method. Eventually, the crack growth paths observed in the experiments are compared with the numerically simulated models. The results obtained show that these central cracks propagate in two ways, which are dependent on their initial angle. By increasing the initial crack angle to greater than 30° (α > 30°), the wing crack path moves further away from the initial crack, and by decreasing α to smaller than 30° (α < 30°), only the shear cracks are initiated. Therefore, the validity and accuracy of the results are manifested by comparing all the corresponding results obtained by different methods. Based on these results, it can generally be concluded that the strength of the cubic (rock material) specimens increases with increase in the crack angles with respect to the applied loading direction.